This file was created by the TYPO3 extension bib --- Timezone: CET Creation date: 2021-03-03 Creation time: 01-09-21 --- Number of references 1 article Hell:2011a ISIJ International 2011 51 10 1724-1732 We elaborated two carbide-free bainitic steels with different microstructures through specific alloy design and austempering process. Microstructural characterizations were performed by means of EBSD analysis and in-situ high energy synchrotron diffraction in order to evaluate the phase fractions and the carbon content in the retained austenite, as well as the microtextures. These microstructural features were correlated to the tensile properties. Both steels exhibited an excellent compromise between high strength (above 1 250 MPa), good ductility (uniform elongation up to 14%) and high fracture strain (reduction of area up to 46%). The volume fraction of MA blocks (blocks of retained austenite partially transformed into fresh martensite during the final cooling at room temperature) was a key relevant parameter that strongly influenced the work-hardening at the expense of the damaging processes at high strain. Département SI2M : Microstructures et Contraintes 0915-1559 Jean-ChristopheHell MoukraneDehmas SebastienAllain Juscelino MendesPrado AlainHazotte Jean-PhilippeChateau