This file was created by the TYPO3 extension bib --- Timezone: CET Creation date: 2021-01-27 Creation time: 15-34-39 --- Number of references 2 article Horwat2012 Chemistry of materials 2012 24 (3) 2429-2432 Département SI2M : Microstructures et Contraintes 10.1021/cm301179x D.Horwat M.Dehmas A.GUTIERREZ J.F.Pierson A.Anders F.SOLDERA J.L.Endrino article Horwat:2012 Journal of Physics and Chemistry of solids 2012 73 4 554-558 Zr1-xWx nanocrystalline films of Zr-W solid solutions and ZrW2 Laves phase were synthesized by magnetron co-sputtering. Large values of the H/E ratio up to 0.09 are observed for grain sizes in the nanometer range along with a hardness above 10 GPa and Young's modulus below 230 GPa. H/E values are correlated with the developed surface of grain boundaries suggesting an elastic deformation mostly handled by the grain boundaries. This is associated to friction coefficients comparable to those of metallic glass surfaces. In contrast to fragile bulk Laves phases, no cracks were detected at the film surface after indentation and scratch test of nanocrystalline ZrW2. The friction coefficient of such films against diamond tip was in the range 0.08-0.15, similarly to metallic glass surfaces. (C) 2011 Elsevier Ltd. All rights reserved. Département SI2M : Microstructures et Contraintes 0022-3697 10.1016/j.jpcs.2011.12.009 D.Horwat E.JIMENEZ-PIQUE J. F.Pierson S.Migot M.Dehmas M.Anglada