This file was created by the TYPO3 extension bib --- Timezone: CET Creation date: 2021-01-25 Creation time: 03-13-49 --- Number of references 2 article Xiong:2010a In situ transmission electron microscopy investigations of the kinetics of alpha `'-Fe16N2 precipitation during the ageing of nitrogen-ferrite Scripta Materialia 2010 63 (12) 12 1232-1235 In situ transmission electron microscopy investigations were carried out on a supersaturated nitrogen ferrite to characterise the precipitation kinetics of alpha `'-Fe16N2 nitrides at 85 degrees C. The coarsening behaviour consists of two stages. The first stage obeys the LSW theory and the coarsening rate was determined as 11.2 nm(3) s(-1). The second stage corresponds to the stabilization of coarsening, and was assumed to be related to the coherency loss between the precipitates and the matrix. (c) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. Département SI2M : Microstructures et Contraintes 1359-6462 10.1016/j.scriptamat.2010.08.045 X. C.Xiong A.Redjaïmia M.Goune article Xiong:2010 Transmission electron microscopy investigation of acicular ferrite precipitation in gamma `-Fe4N nitride Materials Characterization 2010 6 (11) 11 1245-1251 Acicular shaped crystals precipitate from gamma Fe4N nitride in an iron-nitrogen alloy and were identified by electron microdiffraction as alpha ferrite Acicular ferrite develops both the Nishiyama-Wassermann and the Kurdjumov-Sachs orientation relationships with gamma' Fe4N nitride These orientation relationships were discussed in terms of the symmetry theory The driving force for acicular ferrite formation was related to the increasing nitrogen content of gamma' Fe4N, in equilibrium with alpha ferrite, with decreasing temperature The passage from lamellar to acicular structure in Fe-N system was proposed (C) 2010 Elsevier Inc All rights reserved Département SI2M : Microstructures et Contraintes 1044-5803 10.1016/j.matchar.2010.08.005 X. C.Xiong A.Redjaïmia M.Goune