Brunetti, G., Settefrati, A., Hazotte, A., Denis, S., Fundenberger, J. -J., Tidu, A. and Bouzy, E.
Micron, 43(2-3):396-406
2012
ISSN: 0968-4328

Resume: In single-crystal nickel-based superalloys, the lattice mismatch associated with interface coherency between gamma matrix and gamma' precipitates has a strong influence on mechanical properties. The unconstrained lattice misfit in a single-crystal of the MC2 nickel-based superalloy is determined using convergent beam electron diffraction measurements and finite element calculations. The apparent lattice parameters of both constrained phases are obtained in thin foils, using a new multi-pattern approach, which allows for unambiguous determination of all the lattice parameters considering the real symmetry of the strained crystals. Finite element calculations are used to establish relations between the constrained and unconstrained lattice parameters, with the stress relaxation resulting from the thin foil geometry taken into account. (C) 2011 Elsevier Ltd. All rights reserved.

Equipe: Département SI2M : Microstructures et Contraintes

2011

Articles:

Hell, Jean-Christophe, Dehmas, Moukrane, Allain, Sebastien, Prado, Juscelino Mendes, Hazotte, Alain and Chateau, Jean-Philippe
ISIJ International, 51(10):1724-1732
2011
ISSN: 0915-1559

Resume: We elaborated two carbide-free bainitic steels with different microstructures through specific alloy design and austempering process. Microstructural characterizations were performed by means of EBSD analysis and in-situ high energy synchrotron diffraction in order to evaluate the phase fractions and the carbon content in the retained austenite, as well as the microtextures. These microstructural features were correlated to the tensile properties. Both steels exhibited an excellent compromise between high strength (above 1 250 MPa), good ductility (uniform elongation up to 14%) and high fracture strain (reduction of area up to 46%). The volume fraction of MA blocks (blocks of retained austenite partially transformed into fresh martensite during the final cooling at room temperature) was a key relevant parameter that strongly influenced the work-hardening at the expense of the damaging processes at high strain.

Equipe: Département SI2M : Microstructures et Contraintes